Gvozdenović M.Jugovic, BranimirStevanovic J.Grgur, BranimirTrišović, TomislavKnezevic Jugovic, Zorica2021-04-202021-04-2020110379-6779https://scidar.kg.ac.rs/handle/123456789/9996Electrochemical polymerization of polyaniline (PANI) coating on copper electrode was performed galvanostatically in the current density range between 0.50 and 1.25 mA cm-2, from aqueous solution of 0.3 mol dm -3 sodium benzoate and 0.2 mol dm-3 aniline. The corrosion behavior of PANI coated copper and copper electrode exposed to 0.5 mol dm -3 sodium chloride solution was investigated by potentiodynamic and electrochemical impedance spectroscopy techniques. It was observed that thin PANI (5 μm) coating had provided efficient protection (∼96%) to copper in 0.5 mol dm-3 sodium chloride solution. Unusual initial impedance behavior to that normally observed with conventional organic coatings was attributed to dedoping of benzoate anions from the polymer coating. © 2011 Elsevier B.V. All rights reserved.restrictedAccessarticle10.1016/j.synthmet.2011.04.0292-s2.0-79960012036