Bobić B.Mitrovic, SlobodanBabic, MiroslavVencl, AleksandarBobic, Ilija2023-03-102023-03-102011https://scidar.kg.ac.rs/handle/123456789/17121Corrosion behaviour of the as-cast and heat-treated ZA27 alloy was examined. The alloy was prepared by conventional melting and casting route and then thermally processed by applying T4 heat treatment regime (solutionizing at 370 􀁱C for 3 hours followed by water quenching and natural aging). Corrosion rate of the as-cast and heat-treated ZA27 alloy was determined in 3.5 wt. % NaCl solution through immersion test using both weight loss method and polarization resistance measurements. It was shown that applied thermal treatment resulted in increased ductility of the heat-treatedalloy and had a small beneficial effect on the corrosion resistance of ZA27 alloy.enAttribution-NonCommercial 3.0 United Stateshttp://creativecommons.org/licenses/by-nc/3.0/us/ZA27 alloycorrosionconferenceObject